excellent heat resistant performance in a suitable process conditions
Characteristic: compostable , biological source , biodegradable,low heat resistant, food contact
Used: PLA resin IM9005 is suitable for processing all kinds of heat resistant injection products, such as the disposable coffee cups, cups, etc.
Advantage: biological sources, biodegradable, food contact
-
1. Description & Properties
TJL PLA polymer IM9005 is a thermoplastic resin derived from annually renewable resources and is specifically designed for Injection Molding applications. The table below shows the properties of IM9005.
Appearance: White opaque pellets.
Application：Injection Molding,Food Contacting Materials
Item Unit Data Test Method Density g/cm3 1.24
ISO 1183
Mass flow rate(210℃，2.16kG) g/10min 20-30
ISO 1133
mould shrinkage % 0.1-0.3
ISO 294
Tensile strength at break(10mm/min) MPa 63
ISO 527
Elongation at break(10mm/min) % 6
ISO 527
Flexural strength at break(2mm/min) MPa 100
ISO 178
Flexural modulus(2mm/min) MPa 3500
ISO 178
Notched impact strength(4mm，23℃) kJ/m2 4
ISO179/1eA
Melting point(10℃/min) ℃ 160-170
ISO11357
Heat deflection temperature HDT/B(0.45MPa) ℃ 105
ISO 75
2. Applications & Propertie
- Disposable tableware：plastic cups, plates, coffee cup, spoon and so on;
- Toys：Toys for baby and pat
- Plastics for daily use：comb; stationery
3. Processing Information
1. Drying 2. Injection Molding Temperature Drying Equipment
desiccant dryer
Rear – Zone 1 Temperature
℃
＜140
Drying Temperature
℃
80-90
Middle – Zone 2 Temperature
℃
170-190
Drying Time
h
2-3
Front – Zone 3 Temperature
℃
180-210
ppm
＜200
Nozzle Temperature
℃
190-210
℃
180-210
3.Others Mold Temperature
℃
100-120
Screw Speed
rpm
50-150
Injection Pressure
MPa
8-10